ASTM F104 F712290E33M4
Download Data Sheet
Service Limits
| Type | Description | Value |
|---|---|---|
| Temperature Limits | ||
| Maximum | 750°F (400°C) | |
| Continuous Max | 480°F (250°C) | |
| Pressure Limits | ||
| Maximum | 1560 psi (70 bar) | |
| Continuous Max | 1140 psi (50 bar) | |
| ASTM F104 | Line Call Out | F712290E33M4 |
| Color | Black | |
| Available Sheet Sizes | ||
| Thickness | 1/64", 1/32", 1/16", 3/32", 1/8" | |
| Sheet Sizes | 59" x 63" | |
| 59" x 126" | ||
Typical Physical Properties
| ASTM Test Method | Property | Value |
|---|---|---|
| - | Density | 96 lb/ft^3 (1.7 gm/cc) |
| F36 | Compressibility | 7-17% |
| F36 | Recovery | min 45% |
| F152 | Tensile Strength | 1450 psi (10 N/mm^2) |
| F495 | Ignition Loss | Max 37% |
| F146 | Thickness Increase After 5 Hour Immersion | |
| - | ASTM IRM 903 @ 300°F (150°C) | Max 20% |
| - | ASTM Fuel B @ 77°F (25°C) | Max 15% |
| F136 | Weight Increase After 5 Hour Immersion | |
| - | ASTM IRM 903 @ 300°F (150°C) | Max 25% |
| - | ASTM Fuel B @ 77°F (25°C) | Max 15% |
| F38 | Creep Relaxation | 23% |
| - | Torque Retention (DIN 52913) | 40 N/mm^2 |
| F37A | Sealibility at 1000 psi | 0.3 mL/h |
Construction
Style NA1090 is a compressed non-asbestos sheet gasket material produced from inorganic fibers, reinforced filler and bonded with nitrile rubber (NBR). It is manufactured through the hot calendar process under rigorous quality control standard that are registered under ISO-9001.
Application / Service
Style NA1090 is a general purpose Compressed Non-Asbestos sheet gasket material suitable for services with the following general media categories:
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Comparable to
- Garlock 5500
- Thermoseal (Klinger) C4439